Effect of aluminium on the compressibility of silicate perovskite - Université Pierre et Marie Curie Access content directly
Journal Articles Geophysical Research Letters Year : 2004

Effect of aluminium on the compressibility of silicate perovskite


Volume measurements for aluminous MgSiO3 perovskite containing 5 mol% Al2O3 were carried out up to pressures of 40 GPa at ambient temperature, using monochromatic synchrotron X-ray diffraction. A least-squares refinement of the data to the Birch-Murnaghan equation of state yields the following parameters V-0 = 163.234(8) Angstrom(3), K-T0 = 251.5(13) GPa, K-0' = 4. Within uncertainties, the presence of 5 mol% Al2O3 in MgSiO3 perovskite induces a decrease of the bulk modulus in the range of 0% to 1.8%. Thus, K-T of perovskite is affected little if at all by the presence of Al3+. This result is in excellent agreement with the values deduced from sound velocity measurements on the same sample [Jackson et al., 2004]. We discuss the possible origin of discrepancies among the different bulk moduli reported to date for aluminous perovskite. In light of recent calculations, our results are consistent with aluminium being dissolved in MgSiO3 perovskite through a coupled substitution mechanism involving the replacement of both Mg2+ and Si4+ in the dodecahedral and octahedral sites by 2 Al3+. Moreover, any slight reduction in the bulk modulus of MgSiO3 perovskite induced by the dissolution of 5 mol% Al2O3, indicates that the relative proportions of the minerals characteristic of the lower mantle, as inferred from seismological models, should not be significantly altered by the introduction of Al in the system.
Fichier principal
Vignette du fichier
2004GL020213.pdf (137.46 Ko) Télécharger le fichier
Origin : Publisher files allowed on an open archive

Dates and versions

hal-00232722 , version 1 (01-02-2021)



Isabelle Daniel, Jay D. Bass, Guillaume Fiquet, Hervé Cardon, J. Z. Zhang, et al.. Effect of aluminium on the compressibility of silicate perovskite. Geophysical Research Letters, 2004, 31, pp.L15608. ⟨10.1029/2004GL020213⟩. ⟨hal-00232722⟩
134 View
49 Download



Gmail Facebook X LinkedIn More