Distinctive Arsenic(V) Trapping Modes by Magnetite Nanoparticles Induced by Different Sorption Processes - Université Pierre et Marie Curie Accéder directement au contenu
Article Dans Une Revue Environmental Science and Technology Année : 2011

Distinctive Arsenic(V) Trapping Modes by Magnetite Nanoparticles Induced by Different Sorption Processes

Résumé

Arsenic sorption onto iron oxide spinels such as magnetite may contribute to arsenic immobilization at redox fronts in soils, sediments, and aquifers, as well as in putative remediation and water treatment technologies. We have investigated As(V) speciation resulting from different sorption processes on magnetite nanoparticles, including both adsorption and precipitation, using X-ray absorption fine structure (XAFS) spectroscopy and transmission electron microscopy (TEM). XAFS results suggest that AsO4 tetrahedra form predominantly inner-sphere bidentate corner-sharing (2C) complexes and outer-sphere complexes on magnetite in the adsorption experiments. In the precipitation experiments, an increasing fraction of AsO4 tetrahedra appears to be incorporated in clusters having a magnetite-like local structure with increasing As loading, the remaining fraction of As being adsorbed at the surface of magnetite particles. In the sample with the highest As loading (15.7 μmol/m2) XAFS data indicate that As(V) is fully incorporated in such clusters. Such processes help to explain the significantly higher arsenic uptake in precipitation samples compared to those generated in adsorption experiments. In addition, for the precipitation samples, TEM observations indicate the formation of amorphous coatings and small (∼3 nm) nanoparticles associated with larger (∼20 40 nm) magnetite nanoparticles, which are absent in the adsorption samples. These results suggest that As(V) could form complexes at the surfaces of the small nanoparticles and could be progressively incorporated in their structure with increasing As loading. These results provide some of the fundamental knowledge about As(V)-magnetite interactions that is essential for developing effective water treatment technologies for arsenic
Fichier non déposé

Dates et versions

hal-01054557 , version 1 (07-08-2014)

Identifiants

Citer

Yuheng Wang, Guillaume Morin, Georges Ona-Nguema, Farid Juillot, Georges Calas, et al.. Distinctive Arsenic(V) Trapping Modes by Magnetite Nanoparticles Induced by Different Sorption Processes. Environmental Science and Technology, 2011, 45, pp.258-7266. ⟨10.1021/es200299f⟩. ⟨hal-01054557⟩
130 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More