Impact of a γ-Al<sub>2</sub>O<sub>3</sub>(001) barrier on LaAlO<sub>3</sub> metal-oxide-semiconductor capacitor electrical properties - Université Pierre et Marie Curie Accéder directement au contenu
Article Dans Une Revue Journal of Vacuum Science & Technology B Microelectronics and Nanometer Structures Année : 2009

Impact of a γ-Al2O3(001) barrier on LaAlO3 metal-oxide-semiconductor capacitor electrical properties

Résumé

Amorphous LaAlO3 high-κ oxides were grown in a molecular beam epitaxy reactor on p-Si(001) employing a thin γ-Al2O3 epitaxial layer as buffer. Interfaces are free of SiO2 and silicates and remain abrupt even after high temperature annealing as demonstrated by x-ray photoelectron spectroscopy. Electrical measurements performed on as-deposited samples reveal dielectric constant values close to the bulk ones, small equivalent oxide thickness, and low interface state densities. Some negative charges are present leading to a flatband voltage shift. Postdeposition annealing can correct this effect.
Fichier principal
Vignette du fichier
Becerra2008.pdf (217.3 Ko) Télécharger le fichier
Origine Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-01939927 , version 1 (17-11-2022)

Licence

Identifiants

Citer

L. Becerra, C. Merckling, M. El-Kazzi, N. Baboux, B. Vilquin, et al.. Impact of a γ-Al2O3(001) barrier on LaAlO3 metal-oxide-semiconductor capacitor electrical properties. Journal of Vacuum Science & Technology B Microelectronics and Nanometer Structures, 2009, 27 (1), pp.384-388. ⟨10.1116/1.3065437⟩. ⟨hal-01939927⟩
68 Consultations
41 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More